本研究では、PWRプラント運転を想定した熱時効初期の残留応力緩和メカニズム解明の一環として、LP、WJP、バフ研磨の三工法および機械加工を施した600合金について、熱時効時の組織変化を明確にすることを目的とした。各工法の施工材についてEBSD解析を行うことにより、応力緩和過程に関与すると考えられる組織学的因子の検討を実施した。...
英字タイトル:
Microstructural Investigation of Residual Stress Relaxation Process of Ni-based Alloy by EBSD Analysis

The relaxation behavior of the compressive stress in nickel-based alloy 600 introduced by WJP and buffing stress improving treatments has been investigated. Hardness reduction behavior in WJP and buffing processed samples during thermal aging has been found to follow the Johnson-Mehl-Avrami equation and the rate constant for hardness reduction to be expressed by the Arrhenius equation. EBSD crystal orientation analysis has confirmed that the strain is introduced mainly in the surface region. Positron lifeti...
英字タイトル:
Mechanism for stress relaxation behavior of WJP and buffing stress improving treatments

In order to prevent primary water stress corrosion cracking (PWSCC), water jet peening (WJP) has been used on the welds of Ni-based alloys in pressurized water reactors (PWRs). However, the compressive residual stresses induced by WJP might be relaxed during the actual operation because of the elevated temperature environment. Therefore, the stability of the compressive residual stresses caused by WJP has been investigated during thermal aging. The result shows that the compressive residual stresses has...
英字タイトル:
Relaxation behavior of residual stress generated by water jet peening under operation temperature environment ― Evaluation for long term stability of residual stress improving treatment on Ni base alloy (report 1) ―

Temper bead welding (TBW) is one effective repair welding method for the large-scale nuclear power plants instead of post weld heat treatment (PWHT). Consistent Layer (CSL) technique is the theoretically most authoritative method among the five temper bead welding techniques. For TBW, toughness is the key criteria to evaluate the tempering effect. A neural network-based method for toughness prediction in heat affected zone (HAZ) of low-alloy steel has been investigated to evaluate the tempering effect...
英字タイトル:
Prediction of Toughness in HAZ produced by Temper Bead Welding of Consistent Layer Technique

Abstract For the last couple of years, issue of defects in Alloy 600 weld lowered the capacity factor of nuclear power plants. To apply newly developed repair technique, like temper-bead welding that has not been prescribed in technical standards, it is necessary to evaluate its technical applicability to the requirement. In the previous cases, this process has been completed by issuance of no action letter for specific area and condition, utilizing implementation process, such as confirm testing by J...
英字タイトル:
Study on implementing newly developed repair welding technique within a limited time frame for nuclear power plant

Stress corrosion cracking (SCC) is one of serious aging degradation problems for the Alloy 600 components of pressurized water reactors (PWRs). In order to prevent SCC, various methods such as water jet peening (WJP), laser peening (LP), surface polishing have been used to introduce compressive stresses at the surfaces of the PWR components. However, it has been reported that such compressive residual stress introduced by these methods might be relaxed during the practical operation, because of high te...
英字タイトル:
Kinetic analysis on the long term stability of the effect obtained by various residual stress improvement methods ― Evaluation for long term stability of residual stress improving treatment on Ni base alloy (report 2) ―

In order to estimate the stability of the stress improving effect by water jet peening (WJP) residual stress improvement methods during the long-term operation of nuclear power plants, the residual stress in nickel-based alloy 600 has been studied through the kinetics of hardness reduction behavior in practical operation temperatures. Based on the relationship between the residual stress relaxation and the hardness reduction rates, it has been found that in actual operating condition, when the hardness decr...
英字タイトル:
Prediction of Residual Stress Stability Introduced by Water Jet Peening Residual Stress Improvement Method to Ni-based Alloy during Long-Term Operation

In order to compare the stability of the stress improvement effect introduced by laser peening (LP), water jet peening (WJP) and buffing residual stress improvement methods during the long-term operation of nuclear power plants, the hardness in nickel-based alloy 600 has been studied through the kinetics of hardness reduction behavior in practical operation temperatures. The predicted hardness results show that in actual operating condition, the time required to reduce the hardness to 180HV is 1268 years fo...
英字タイトル:
Long-Term Stability Comparison of LP, WJP and Buffing Residual Stress Improvement Methods under Actual Operating Condition

原子力発電プラントの高経年化に伴い発生する経年劣化事象の一つである応力腐食割れ(Stress Corrosion Cracking: SCC)の防止対策として、溶接に伴って発生した引張残留応力を圧縮残留応力に変化させる応力改善が有効である。 本研究では、材料内部の格子欠陥の存在状態を定量的に、かつ、高感度に評価できる陽電子寿命法を採用することにより、応力改善工法の施工により導入された残留応力に密接に関連する格子欠陥や転位によるひずみの存在を調査した。...
英字タイトル:
Consideration on Mechanism of Residual Stress Relaxation Behavior of Ni-based Alloy Using Positron Annihilation Lifetime Spectroscopy?